著者

水上 智 清水 完 脇谷 尚樹 篠崎 和夫 水谷 惟恭

出版者

公益社団法人日本セラミックス協会

雑誌

日本セラミックス協会学術論文誌 : Nippon Seramikkusu Kyokai gakujutsu ronbunshi (ISSN:18821022)

巻号頁・発行日

vol.110, no.1281, pp.428-431, 2002-05-01

被引用文献数

1 2

---

Epitaxial (Ni-Zn) Fe_2O_4 thin film was prepared on Si (001) substrates using (MgO-Al_2O_3) /CeO_2/YSZ triple buffer layer. In this work, to increase remanent magnetization (M_r) and decrease coercive field (H_c), for epitaxial (Ni-Zn) Fe_2O_4 thin film, the effect of substrate temperature, oxygen pressure and composition on the magnetic properties was examined. It was clarified that the remanent magnetization and coercive field were strongly influenced by temperature and oxygen pressure. In order to obtain high Mr and low H_c, it was thought that a substrate temperature of 800℃ and oxygen pressure 1.3 Pa were optimal conditions. As regarding the composition, M_r could be obtained to a maximum of 3.96 × 10^<-1> Wb/m^2 changing the quantity of Zn and Fe (M_8=5.31 × 10^-1 Wb/m^2, H_c= 1.35 × 10^1 kA/m).

著者

石川 剛

出版者

公益社団法人日本セラミックス協会

雑誌

日本セラミックス協会学術論文誌 : Nippon Seramikkusu Kyokai gakujutsu ronbunshi (ISSN:18821022)

巻号頁・発行日

vol.112, no.1309, pp.507-510, 2004-09-01

被引用文献数

2 3

---

The hydroxapatite coloring phenomenon after high-temperature firing was caused by the kinds of atmosphere gasses and the pressure. Especially the influence of oxygen on the coloring was strong. X-ray diffraction measurement showed that the hydroxapatite coloring phenomenon corresponded to the crystal phase transition of hydroxapatite. The crystal system of white and red hydroxapatite was monoclinic and reddish-brown hydroxapatite was hexagonal. From the measurement of the spectrophotometer, red hydroxapatite had an absorption band near 537 nm. This absorption band was considered to be due to the color center.

著者

飯塚 建興 北 英紀 平井 岳根 大角 和生

出版者

公益社団法人日本セラミックス協会

雑誌

日本セラミックス協会学術論文誌 : Nippon Seramikkusu Kyokai gakujutsu ronbunshi (ISSN:18821022)

巻号頁・発行日

vol.111, no.1299, pp.837-840, 2003-11-01

---

MoSi_2とMo_5Si_3粒子強化窒化ケイ素(Si_3N_4)複合材料は高強度,高靭性,耐摩耗性,耐酸化性と低摩擦性等において優れた特性を有しているので,耐摩耗部材や高温用部材として注目されている.MoSi_2とMo_5Si_3粒子強化Si_3N_4複合材料はそれぞれMoSi_2粉末を混合したSi_3N_4の成形体,又はモリブデン溶液を含浸させたSi_3N_4の仮焼体を高温で焼成することにより作製できる.MoSi_2粒子強化Si_3N_4複合材料では,MoSi_2粒子の粒径は出発原料であるMoSi_2粉末の粒径に依存し,1μm以上となるが,Mo_5Si_3粒子強化Si_3N_4複合材料では,含浸法でSi_3N_4の仮焼体に分散させた酸化モリブデンは高温焼成のプロセスでSi_3N_4と反応し,平均粒径0.1μmの球状Mo_5Si_3粒子はSi_3N_4の粒界ガラス相にその場で生成することが可能である.しかし,Mo_5Si_3粒子強化Si_3N_4複合材料では,Mo_5Si_3球状粒子の生成と同時に,酸窒化ケイ素(Si_2N_2O)針状,又は板状粒子も生成した.MoO_3の添加量の増加に伴って,Mo_5Si_3-Si_3N_4複合材料中のSi_2N_2Oの量が増加し,またその形状は針状から板状に変化する.含浸法で6mass%以下のMoO_3を添加した場合,複合材料の曲げ強度は向上したが,それ以上のMoO_3を添加すると,低強度の板状結晶粒子Si_2N_2Oが大量に生成するため,複合材料の強度は低下した.通常,Si_2N_2OはSi_3N_4とシリカに金属酸化物等の焼結助剤を添加した原料粉末を焼結することにより作製され,Si_2N_2Oの機械的性質はSi_3N_4より劣るが,その耐酸化性はSi_3N_4より優れている.このように,多くのMo_5Si_3粒子を複合したSi_3N_4複合材料の機械的性質を更に改善するには,なるべくSi_2N_2Oの生成を抑えることが必要である.一方,その耐酸化性を改善するには,逆にSi_2N_2Oの量を増やした方が有効だと考えられる.そこで,本研究では金属モリブデン粉末と酸化モリブデンの前駆体であるヘプタモリブデン酸アンモニウム四水和物を使って,多量のMo_5Si_3粒子をその場で生成させると同時にSi_2N_2Oの生成量を極力に抑えたMo_5Si_3粒子強化Si_3N_4複合材料とMoO_3とSi_3N_4の反応を利用し逆にSi_2N_2Oを大量に生成させたMo_5Si_3粒子強化Si_2N_2O複合材料の作製を試み,その微構造と機械的性質を評価した.

著者

小嶋 芳行 川野辺 晃生 安江 任 荒井 康夫

出版者

公益社団法人日本セラミックス協会

雑誌

日本セラミックス協会学術論文誌 : Nippon Seramikkusu Kyokai gakujutsu ronbunshi (ISSN:18821022)

巻号頁・発行日

vol.102, no.1192, pp.1128-1136, 1994-12-01

被引用文献数

20 23

---

In this report, controls of polymorphism and morphology of calcium carbonate compounds were studied by suspending amorphous calcium carbonate hydrate (ACC) powder in water or MgCl_2 solution. Characteris tics of calcium carbonate compounds formed from ACC were determined by means of X-ray diffraction, thermal analysis (TG-DTA) and scanning electron microscopic observation. ACC was synthesized by adding 0.1mol dm^<-3> CaCl_2 solution into a mixed solution of 0.1 mol dm^<-3> NaOH and 0.1 mol dm^<-3> Na_2CO_3 at 0℃. The calcium carbonate compounds formed easily by suspending ACC in water and was affected remarkably by temperature (0-80℃) and pH (1.7-14.0).Thus ACC changed into hexagonal plate-like calcium carbonate hexahydrate at 0℃, rhombohedral calcite at 15-20℃, spherical vaterite at 30-50℃ and needle like aragonite above 80℃ after aging for 1h. ACC was also changed into vaterite in the pH region of 7.0-9.5 and to basic calcium carbonate above pH 12.8 at 20-40℃. On the other hand, spherical calcium carbonate monohy drate was formed from ACC in MgCl_2 solution (0.03-0.50 mol dm^<-3>) and then changed finally to aragonite after long aging. For example, the amount of spherical monohydrate with a diameter of 30 μm reached a maxi mum after aging for 3d, and it changed to needle like aragonite with an average length of 50 μm after 10d in 0.10 mol dm^<-3> MgCl_2 solution. Accordingly, ACC changed easily to calcium carbonate anhydrides (cal cite, aragonite, vaterite), calcium carbonate hydrates (monohydrate, hexahydrate) and basic calcium car bonate, when ACC was suspended in solutions of different conditions such as ternperature, pH and concentration of MgCl_2.

著者

中野 秀之 奥田 匠昭 右京 良雄

出版者

公益社団法人日本セラミックス協会

雑誌

日本セラミックス協会学術論文誌 : Nippon Seramikkusu Kyokai gakujutsu ronbunshi (ISSN:18821022)

巻号頁・発行日

vol.109, no.1275, pp.974-977, 2001-11-01

被引用文献数

1

---

Hydrothermal synthesis of lithium manganese oxide with α-NaFeO_2 structure has been studied. A Li_xMnO_2 nH_2O, (Li-birnessite), with rhombohedral symmetry was used as a starting material. When the molar ratio of Mn/Al was smaller than 0.9/0.1, spinel type lithium manganese oxides were obtained. On the other hand, when the molar ratio of Mn/Al was larger than 0.85/0.15, metastable lithium manganese oxides with α-NaFeO_2 structure formed at 80℃, and the capacity fade of the Li-ion cell with cathodes made of these oxides was very small in comparison with that of cathodes made of layered Li-manganese oxides, as previously reported.

著者

Griscom David L.

出版者

公益社団法人日本セラミックス協会

雑誌

日本セラミックス協会学術論文誌 : Nippon Seramikkusu Kyokai gakujutsu ronbunshi (ISSN:18821022)

巻号頁・発行日

vol.99, no.1154, pp.923-942, 1991-10-01

被引用文献数

36 533

---

この論文では,シリカガラスと他のアモルファスSiO_2型における点欠陥の構造と光学的性質について何が知られているを解説する.現在入手できる構造の情報は,主に電子スピン共鳴分光(ESR)-常磁性を示す欠陥の副クラスにのみ直接適応できる方法-の結果から得られている.ESRによってこれまでに同定された固有型常磁性中心としては,E'中心(≡Si・),非架橋酸素ホール中心(≡Si-O・),過酸素ラジカル(≡Si-O-O・)と自己捕捉ホールがある.シリカ中で生じると考えられる固有型反磁性欠陥の例としては中性の酸素空格子(≡Si-Si≡),二配位のケイ素原子(-O-Si-O-)と過酸素結合(≡Si-O-O-Si≡)がある.最も共通した非固有型欠陥は水酸基と塩化物の不純物と関連したものである.照射誘起されたH^0とH_2は,OHを100ppm以上含むガラス中における欠陥の,照射後の成長と減衰速度に重要な役割を果たす.文献からESR/光学の相互関係をまとめると,可視,紫外,VaCuum-紫外分光域における多くの欠陥と関連した光学的吸収バンドの最も有り得る起因は,その相互関係に包含される.これらのバンドの他のものは,格子間O_2,O_3,Cl_2分子によるものであり,それはそれら分子のスペクトルの位置と幅がガス中の対応する種のものと類似しているからである.