著者

伊藤 孝矩 山﨑 重人 光原 昌寿 中島 英治 西田 稔 米村 光治

出版者

一般社団法人 日本鉄鋼協会

雑誌

鉄と鋼 (ISSN:00211575)

巻号頁・発行日

pp.TETSU-2016-107, (Released:2017-03-06)

参考文献数

37

被引用文献数

4

---

Creep properties and microstructures for a polycrystalline Ni-based heat-resistant alloy whose grain boundaries were covered by dense intergranular intermetallics were investigated. Creep tests were carries out at 850°C and 80-130 MPa. The creep strength of this alloy was higher than the Alloy617 and HR6W, and equal to the Alloy740, which are pre-existing candidate materials for steam pipes of A-USC power plant. The retardation of acceleration of creep rate was observed characteristically in the creep curves. This retardation behavior was deeply related to the superior creep strength of this alloy. The spherical Ni3Al (γ’) particles were distributed uniformly in the grain interior, whose coarsening behavior was monotonically dependent on the creep time. The intermetallics of Laves phase and σ pahse were formed densely at grain boundary. High coverage ratio of the intergranular intermetallics was maintained until the later stage of acceleration creep region. Therefore, it suggested that the retardation of creep acceleration was not caused by the precipitates behavior of intragranular γ’ particles and intergranular intermetallics, though both the precipitates were understandably effective against the creep strengthening. The plate-like Laves phase was formed in the grain interior during creep. The evolution of volume fraction of intragranular Laves phase depended on not creep time but creep strain. From the results of SEM/EBSD analyses and TEM observations, it revealed that the intragranular Laves phase enhanced the work-hardenability due to the constraint on plasticity and originated the retardation of creep acceleration.

著者

河村 能人 萩原 幸司 相澤 一也 木村 滋 古原 忠 東田 賢二 乾 晴行 奥田 浩司 中谷 彰宏 君塚 肇 中島 英治 大橋 鉄也

出版者

熊本大学

雑誌

新学術領域研究(研究領域提案型)

巻号頁・発行日

2011-04-01

---

総括班の役割は、各計画研究と公募研究が緊密に連携して十分な研究成果が出せるように、本領域の組織的かつ効果的な運営と研究支援活動ならびに若手人材育成を図り、本領域の目的達成と次への展開に資することである。運営面での特徴は,①6つの部会と4つの事務局による効率的な運営、②量子線共同利用施設や共通試料提供等による研究支援、③若手人材育成への注力、④国際交流,異分野交流,産学官交流の推進である。総括班としての主な成果は、各種領域内会議による効果的な運営、研究支援による効率的な研究推進、領域内交流による連携推進、国内外シンポジウム等の開催による本領域のプレゼンス向上、若手研究者の活躍等である。