Epoxy resin composites containing steel grinding chips as a conducting filler was subjected to heat cycling tests in order to evaluate the thermal stability of electrical resistance. The effect of the content of grinding chips, magnetization and precure temperature in the curing process was examined and this resulted in finding the thermal stability to depend mainly on the precure temperature: the higher the precure temperature, the higher was the thermal stability. There was also shown to be a minimum value hi the electrical resistance of the composites at the temperature between 50 and 1OO℃.The ratio to the minimum resistance was found to depend mainly on the precure temperature. It has therefore been clarified that the thermal coefficient of the electrical resistance in the epoxy composites can be controlled by adjusting the precure temperature in the during process.

著者

山田 英介 林 明徳 稲垣 慎二 岡本 弘 古川 淳二

出版者

一般社団法人 日本ゴム協会

雑誌

日本ゴム協会誌 (ISSN:0029022X)

巻号頁・発行日

vol.67, no.9, pp.645-650, 1994

---

ミラブル形およびワンショット法ポリウレタンに対して官能基を有するカルボン酸アルミニウム塩(活性充てん剤)の配合試験を行った. ミラブル形ポリウレタンにおいては, 活性水素をもつ官能基を含有するものを配合すると, ポリウレタンの分解が起こり, 架橋物が得られなかったが, ビニル基を含有するものは, 架橋ポリウレタンの引張り物性を大幅に向上させることを認めた. この架橋物の応力-ひずみ曲線をMooney-Rivlin 式で解析した結果, 活性充てん剤は一次結合の増加に寄与し, 架橋助剤として作用していると考えられる.<br>ワンショット法ポリウレタンでは, ビニル基よりもアミノ基を有する充てん剤の方がイソシアナート基との反応により, 補強効果が大きいことを認めた.

著者

吉川 俊夫 山田 英介 中原 崇文

出版者

合成樹脂工業協会

雑誌

ネットワークポリマー (ISSN:13420577)

巻号頁・発行日

vol.23, no.3, pp.128-133, 2002

---

エポキシ/研磨粉系の導電性硬化物について, 150℃での加熱サイクルテストを行い, 抵抗の熱安定性を測定した。その結果, 高いプレキュア温度を用いて硬化させた試料ほど熱安定性が高いことがわかった。一方, 抵抗値と温度の関係を測定したところ, 極小値を持つU字型曲線を示すことがわかった。更に, 高いプレキュア温度で硬化させた試料ほど曲線が高温側にシフトし, 抵抗値の温度変化が少ないことがわかった。