著者
柴田 芳昭 今濱 敏信 和気 敏治 関根 功 川瀬 哲也 城元 孝之 湯浅 真
出版者
Japan Society of Corrosion Engineering
雑誌
Zairyo-to-Kankyo (ISSN:09170480)
巻号頁・発行日
vol.41, no.8, pp.525-534, 1992-08-15 (Released:2009-11-25)
参考文献数
36

The effect of tannic acid on the corrosion of mild steel in boiler systems was investigated by physicochemical methods using an autoclave and a test boiler. Tannic acid was found to be a good oxygen scavenger at pH 11 as well as hydrazine and sodium sulphite. Tannic acid inhibited corrosion of steel (i) at room temperature and atmospheric pressure and (ii) at high temperature and pressure. The maximum inhibition efficiency was about 97%. The inhibiting behavior of tannic acid at pH 7 was different from that at pH 11. At pH 7, tannic acid acted as an adsorption-type inhibitor and suppressed catholic reaction of corrosion of steel. At pH 11, tannic acid inhibited corrosion of steel not only as an effective oxygen scavenger but also an effective Schikorr reaction promoter (formation of Fe3O4). Tannic acid is believed to be an effective inhibitor in boiler systems.
著者
長谷 隆司 中山 武典 尾関 寿美男 坂西 敏之
出版者
公益社団法人 腐食防食学会
雑誌
Zairyo-to-Kankyo (ISSN:09170480)
巻号頁・発行日
vol.61, no.3, pp.93-97, 2012 (Released:2012-10-31)
参考文献数
11

超電導マグネットによる7.0 Tの磁束密度の磁場を印加することによって,通常の磁場を印加しない場合(NMT)に比べて,流動水中の普通鋼板のさびをより抑制できることが判明した.X線回折の定量分析結果は,さびの抑制に役立つと見られるアモルファスやナノサイズのさびの結晶の量の増加に,水の磁気処理(MT)が有効であることを支持している.NMTとMTの両方の場合で流動水が流れる配管の内部をモニタする実験を行って,MTの場合に配管内の鉄さびの付着をより抑制することがわかった.
著者
瀬尾 眞浩
出版者
公益社団法人 腐食防食学会
雑誌
Zairyo-to-Kankyo (ISSN:09170480)
巻号頁・発行日
vol.61, no.9, pp.341-348, 2012-09-15 (Released:2013-03-01)
参考文献数
44
被引用文献数
3 5

アンダーポテンシャル析出(UPD)とは,水溶液中の金属イオンMz+が金属Mとして析出する平衡電位よりも貴な電位領域で異種金属M'上に析出する現象である.UPDの一般的特徴について述べ,UPDが起きる電位領域の幅はM'とMの仕事関数の差に比例することを強調した.また,酸素還元反応,水素発生反応および金属腐食反応に及ぼすUPDの影響について述べ,反応機構に及ぼすUPD金属の役割を説明した.特にNi 基合金の微量Pbによる応力腐食割れに関連して,PbのUPDがNiの腐食に及ぼす影響について詳しく紹介した.さらに,UPD層の吸着構造から表面合金構造への変化やUPD金属と電解質アニオンの共吸着構造についても触れ,反応機構に及ぼすUPD金属の役割を明らかにするには電極界面のその場解析の重要性を指摘した.
著者
中川 雅晴
出版者
Japan Society of Corrosion Engineering
雑誌
Zairyo-to-Kankyo (ISSN:09170480)
巻号頁・発行日
vol.53, no.3, pp.112-117, 2004-03-15 (Released:2011-12-15)
参考文献数
24
被引用文献数
5 3

現在, チタン製の口腔インプラントや歯科修復物の臨床応用が増加しているが, う蝕予防のために多用されるフッ素によってチタンやチタン合金が腐食することが問題となっている. 本研究では, フッ素含有環境における純チタン, Ti-6Al-4V, Ti-6Al-7Nb合金および新しく試作したTi-(0.1~2.0)wt%Pt (またはPd) 合金の腐食挙動を動電位分極測定, 腐食電位測定によって検討した. また試験溶液に浸漬する前と後の試料表面のSEM観察を行った. 試験溶液として0.1%および0.2%NaF (それぞれ453および905ppmのフッ素濃度に対応) を含有する人工唾液と溶存酸素濃度が低い人工唾液を用いた. フッ素を含有する酸性環境 (pH 4.0) では, 純チタン, Ti-6Al-4V, Ti-6Al-7Nb合金の試料表面は腐食によって顕著に粗造になったが, Ti-Pt (またはPd) 合金はほとんど影響を受けなかった. 溶存酸素濃度が低い環境では, 市販のハミガキ剤に含まれるフッ素濃度 (フッ素濃度として約1,000ppm) では, Ti-Pt (またはPd) 合金は腐食の影響を全く受けなかったが, 純チタン, Ti-6Al-4V, Ti-6Al-7Nb合金は微視的な腐食によるダメージを受けた. Ti-0.5wt%Pt (またはPd) 合金は, フッ素含有環境でも腐食しない高耐食性を有する新しい歯科用チタン合金として応用が期待される
著者
和田 史博
出版者
公益社団法人 腐食防食学会
雑誌
Zairyo-to-Kankyo (ISSN:09170480)
巻号頁・発行日
vol.48, no.12, pp.771-775, 1999-12-15 (Released:2009-11-25)
参考文献数
3
被引用文献数
7 21

JNFL's Rokkasyo Reprocessing Plant (RRP) is under construction in Rokkasyo village Aomori prefecture, and it is required to select appropriate materials of equipment which possess high degree of corrosion resistance to process solutions based on nitric acid. In other existing reprocessing plants, some troubles caused by corrosion of stainless steel has been reported, and almost of these troubles had been occurred at the equipment used in boiling nitric acid condition. In consideration of these experiences and results, in RRP, distillation under reduced pressure technology adopted and zirconium was selected for boiling nitric acid condition under normal pressure.
著者
升岡 正 黛 正己 新井 拓 谷 純一
出版者
公益社団法人 腐食防食学会
雑誌
Zairyo-to-Kankyo (ISSN:09170480)
巻号頁・発行日
vol.56, no.3, pp.93-98, 2007-03-15 (Released:2007-08-31)
参考文献数
17
被引用文献数
8 13

冷間圧延により圧下率を10%から40%まで変化させた低炭素ステンレス鋼SUS316L材を用いてCT試験片を製作し,BWR炉水模擬環境におけるSCCき裂進展試験を実施した.試験では一定荷重を与えコンパクト型 (1 T-CT) 試験片の初期応力拡大係数が20 MPa√mあるいは30 MPa√mになるようにした.マイクロビッカース硬さ (平均値:Hv) の増加に伴い,き裂進展速度は増大する傾向を示し,Hv 250以上では熊谷らによる加工硬化材の割れ進展速度暫定線図より大きな進展速度を示した.しかし,これら硬さ (圧下率) の大きい試験片の割れ形態はシュラウド熱影響部などに生じたSCC損傷と異なり粒内型SCCが支配的であった.一方,Hv 230 (圧下率 10%) の条件の試験片ではほぼ完全な粒界割れとなり,実機に生じたSCCと同様の割れ形態であった.これらの結果から,冷間加工材に対するき裂進展試験を行う際には,破面形態を十分に考慮し,実機と同等な破面を呈する加工度の試験片を用いる必要性が示唆された.
著者
藤田 敏雄
出版者
Japan Society of Corrosion Engineering
雑誌
Zairyo-to-Kankyo (ISSN:09170480)
巻号頁・発行日
vol.43, no.9, pp.511-519, 1994-09-15 (Released:2009-11-25)
参考文献数
11
被引用文献数
2 1

In general, a volatile corrosion inhibitor is the liquid or the solid reagent as the compound or the several mixture which is vaporized (sublimated) slowly at the normal temperature.The resulting vaporized gas has the corrosion inhibiting reaction by the chemical or physical adsorption on metal surface.In Japan, the material with this volatile corrosion inhibitor which is coated on the material, or impregnated into, or extruded into paper or film, is referred to as the “volatile corrosion inhibiting paper” or the “volatile corrosion inhibiting film” respectively, and in which this one is dissolved referred to as the “volatile corrosion inhibiting oil”.We give a general name to above inhibitors referred to as the “volatile corrosion inhibiting material”.This report comments on the summary of kind, standard, nature, property, use and application method and the future trend of these materials.
著者
腐食コスト調査委員会
出版者
公益社団法人 腐食防食学会
雑誌
Zairyo-to-Kankyo (ISSN:09170480)
巻号頁・発行日
vol.50, no.11, pp.490-512, 2001-11-15 (Released:2011-12-15)
参考文献数
10
被引用文献数
15 38

The first report on the cost of corrosion in Japan had been published at 1977. The report estimated that the corrosion loss in Japan which did not include indirect loss was 1-2 percent of Gross National Product (GNP) at that time. Since then, almost two decades have been passed and the industrial structure has drastically changed. Corresponding to this situation, the committee on the cost of corrosion in Japan was organized at 1999 jointly by Japan Society of Corrosion Engineering (JSCE) and Japan Association of Corrosion Control (JACC). The project was funded by the National Research Institute for Metals (NRIM) in the program of the Ultra-Steels (STX-21) Project. Cost of corrosion at 1997 was estimated by the Uhlig method and the Hoar method. The estimated cost was compared with the past data which was estimated at 1974 by the same Uhlig and Hoar method. In addition to the above estimation, the preliminary analysis by the Input/Output method is performed for estimating the total cost of corrosion including the direct and indirect cost. The overall cost estimated by the Uhlig and Hoar method at 1997 was found to be 3, 938 billion yen and 5, 258 billion yen, respectively, which is equivalent to 0.77% and 1.02% to GNP of Japan. The total cost including the direct and indirect cost, which is estimated preliminary by the Input/Output analysis, is likely to be more than 2 times larger than the direct cost estimated by the Uhlig method.
著者
鈴木 智康 小野 孝也 髙橋 賢 野田 和彦
出版者
公益社団法人 腐食防食学会
雑誌
Zairyo-to-Kankyo (ISSN:09170480)
巻号頁・発行日
vol.68, no.5, pp.112-115, 2019-05-10 (Released:2019-10-25)
参考文献数
7
被引用文献数
5 4

物理現象としての結露時におけるACM(Atmospheric Corrosion Monitor)センサの出力挙動と腐食量の関係を明らかにするため種々の試験を行った.結露時のセンサ出力は降雨でのぬれや付着塩の吸水と比較して挙動が異なるため,切り分けて評価する必要があることがわかった.いずれの現象においても,その場測定(in situ)によって得られた出力と腐食量には相関が認められたので,ACMセンサ出力から短時間での腐食速度の推定が可能と考えられる.
著者
細矢 雄司 篠原 正 押川 渡 元田 慎一
出版者
Japan Society of Corrosion Engineering
雑誌
Zairyo-to-Kankyo (ISSN:09170480)
巻号頁・発行日
vol.54, no.8, pp.391-395, 2005-08-15 (Released:2011-12-15)
参考文献数
13
被引用文献数
6 17

炭素鋼の大気腐食における環境の腐食性について, 付着海塩が吸水することによって表面に形成される水膜の厚さの影響を中心に検討した.付着海塩への吸着水量を種々の条件下で実測し, 形成された液膜の濃度を計算値と比較して熱力学計算が実験結果をよく再現する条件を得た. また種々の条件下で炭素鋼の腐食試験を行い, 熱力学計算で導出される水膜の厚さdと腐食速度CRとの関係について調べた. d=50μm近傍においてCRは最大値約0.07mgm-2s-1を取ることを見い出した.
著者
杉本 克久
出版者
Japan Society of Corrosion Engineering
雑誌
Zairyo-to-Kankyo (ISSN:09170480)
巻号頁・発行日
vol.48, no.11, pp.673-680, 1999-11-15 (Released:2009-11-25)
参考文献数
30
被引用文献数
8 9

Electrochemical Impedance Spectroscopy (EIS) has been known as a powerful tool for analyzing electrode reaction mechanism. In this review the history of EIS, the definition of electrochemical impedance, the general concept of transfer function, and the measurement method of electrochemical impedance using a transfer function analyzer are first introduced. Then, analytical methods of impedance spectra using electrical equivalent circuits and the kinetic theory of electrochemical reactions are stated. Finally, the future scope of EIS is briefly given.
著者
栁瀨 幸紀 石川 雄一 酒井 潤一
出版者
公益社団法人 腐食防食学会
雑誌
Zairyo-to-Kankyo (ISSN:09170480)
巻号頁・発行日
vol.63, no.5, pp.329-332, 2014-05-15 (Released:2014-12-13)
参考文献数
5
被引用文献数
1

本研究は保温材下模擬環境における炭素鋼の腐食に及ぼす金属表面温度と濡れ時間の影響を明らかにすることを目的として行った.試料には炭素鋼SS400を用いた.保温材下模擬腐食試験は40℃~200℃の種々の温度に加熱したプレートヒーター上に試料を乗せ,その上にケイ酸カルシウム保温材を乗せ,その保温材に水分を注水することで行った.また,ACMセンサーを用いて保温材下模擬環境における金属表面の濡れ時間の推定を行った.試験の結果,金属表面温度が100℃以上では発錆が認められなかった.また,40℃~90℃では局所的に発錆が見られ,その侵食深さは温度の低下に伴い深くなった.これは,ACMセンサーによる保温材下金属表面の濡れ時間測定結果およびアレニウスの式による温度と腐食速度の関係より,温度の増大に比して濡れ時間の影響が大きいためであることが明らかになった.
著者
貝沼 重信 山本 悠哉 伊藤 義浩 押川 渡
出版者
公益社団法人 腐食防食学会
雑誌
Zairyo-to-Kankyo (ISSN:09170480)
巻号頁・発行日
vol.60, no.11, pp.497-503, 2011-11-15 (Released:2012-04-21)
参考文献数
12
被引用文献数
9 12

鋼構造物を腐食による致命的損傷に対して,安全に供用するためには,部材・部位レベルの腐食環境を定量的に把握した上で,その経時腐食挙動を評価することが重要になる.本研究ではFe/Ag対で構成されるACM型腐食センサーを用いて,降雨の影響を受ける無塗装普通鋼板の経時腐食挙動を評価するための方法を提案することを目的とした.そのために,無塗装普通鋼板を用いた大気暴露試験を行った.また,試験体の表裏面における腐食環境と平均腐食深さの関係を定量評価するために,それらの腐食環境をACM型腐食センサーによりモニタリングした.
著者
丸山 俊夫
出版者
Japan Society of Corrosion Engineering
雑誌
Zairyo-to-Kankyo (ISSN:09170480)
巻号頁・発行日
vol.45, no.8, pp.495-498, 1996-08-15 (Released:2009-11-25)
参考文献数
4
被引用文献数
1 2
著者
藤井 秀樹
出版者
公益社団法人 腐食防食学会
雑誌
Zairyo-to-Kankyo (ISSN:09170480)
巻号頁・発行日
vol.60, no.5, pp.248-253, 2011-05-15 (Released:2011-11-05)
参考文献数
27
被引用文献数
7 8

純チタンおよびチタン合金における水素脆化および関連現象を紹介した.水素脆化は水素化物の生成と密接に関係しており、顕著な量の水素化物が存在する場合、衝撃試験など切欠き付き試験片を用いた高歪み速度試験で脆化が確認できる.定荷重き裂伝ぱ試験など静的な低歪み速度試験では、き裂先端への水素拡散と水素化物生成により脆化すると考えられている.多量のMoやVを含むβ型合金は水素化物が生成しにくく脆化しにくい.
著者
鈴木 智康 小野 孝也 髙橋 賢 野田 和彦
出版者
公益社団法人 腐食防食学会
雑誌
Zairyo-to-Kankyo (ISSN:09170480)
巻号頁・発行日
vol.68, no.8, pp.201-204, 2019-08-10 (Released:2020-01-24)
参考文献数
11
被引用文献数
1 1

淡水中における金属の腐食性モニタリングの検討を目的とし,種々の水溶液中にACMセンサ(Atmospheric Corrosion Monitor Sensor)を浸漬してその出力電流測定を行った.その結果,水温の変化や微量の水処理剤添加に対する瞬間的な応答を確認したことで,ACMセンサがごく短時間で腐食性の変化を出力として捉えられることがわかった.4種の淡水に対しては異なる出力を示し,RCMセンサ(Resistmetric Corrosion Monitor)での腐食量測定値との相関が高いこともわかった.従って,ACMセンサによって淡水系での腐食性モニタリングの可能性が得られた.
著者
中島 博志
出版者
Japan Society of Corrosion Engineering
雑誌
Zairyo-to-Kankyo (ISSN:09170480)
巻号頁・発行日
vol.50, no.3, pp.81-87, 2001-03-15 (Released:2011-12-15)
参考文献数
20
被引用文献数
1

This report gives an outline of corrosion and anticorrosion issues in relation to building and building equipment. There are two types of corrosion. One spoils the beauty of the building, and the other spoils function of the building.Corrosion, which spoils the beauty, is usually induced by the atmospheric phenomena. Economical and easy-maintenance anticorrosion system should be developed such as combination of ACM (atmospheric corrosion measuring) sensor and washer.The causes of corrosion, which spoils function, are mainly classified into macro-galvanic-cell corrosion, and unintended environmental condition such as condensation, oxidizing agent (e.g. chlorine gas), and pH (e.g. carbon dioxide and hydrogen sulfide). The building is composed of the materials of wide-use so that defect of materials (e.g. welded area of stainless steel and carbon membrane of soft copper tube) is less likely to be the cause of corrosion. Therefore, effective anticorrosion can be planned during design phase of the building. Unfortunately, few architects and engineers have proper understandings about anticorrosion method.It is not tolerated that the materials which can survive several decades, are abandoned within few years. Total amount of building materials is so enormous that small loss ends up to the incredibly huge loss. Global and nation-wide actions should be considered.
著者
篠原 正
出版者
公益社団法人 腐食防食学会
雑誌
Zairyo-to-Kankyo (ISSN:09170480)
巻号頁・発行日
vol.63, no.4, pp.116-120, 2014-04-15 (Released:2014-11-14)
参考文献数
31
被引用文献数
4 9

大気腐食は,結露あるいは降雨などの薄い水膜の下で発生し,進展する.水膜の組成は,大気汚染物質沈着速度に依存し,大気の湿度および温度条件ともに変化する.多くのセンサや測定法が,大気環境の腐食性あるいはその環境中での腐食挙動を評価するため開発された.本稿では,それらのセンサや測定法によって評価される,水や付着物あるいは環境因子の役割に基づいて,大気腐食研究の現状と将来展望について述べる.
著者
小野 孝也 鈴木 智康
出版者
公益社団法人 腐食防食学会
雑誌
Zairyo-to-Kankyo (ISSN:09170480)
巻号頁・発行日
vol.68, no.2, pp.42-45, 2019-02-10 (Released:2019-07-26)
参考文献数
17

ぬれ環境下における腐食速度検討のため,各種濃度のNaCl水溶液中にFe/Ag対ACM(Atmospheric Corrosion Monitoring)センサを浸漬して出力電流測定およびFe-Ag間電位差測定を行った.また,RCM(Resistmetry Corrosion Monitor)センサによって実腐食量を求め,ACMセンサの出力と比較した.その結果,実腐食量とACMセンサ出力には明らかな相関が認められ,ACMセンサの出力電流に比べてFe-Ag間電位差の方が優れていることがわかった.従って,雨が直接かからない環境下では従来の出力電流値を用い,ぬれ環境下ではFe-Ag間電位差を用いることで精度の高い腐食速度推定が可能と考えられる.また,この方法はACMセンサの長寿命化にも寄与できると考えられる.